This week, I tried to make a large number of MgF2 nanomembranes for my collaboration with Kevin Webb. I wanted to keep the evaporated surface as pristine as possible, so instead of using the Kapton tape to attach the chips to the platen on its face, I used double sided kapton tape. Our reserves of…
We received W648 from the production team this week. Upon inspection of this wafer, is has a higher density of pinholes than we have been seeing lately (>3 pinholes/slit compared to 0 or 1/slit) and seems to show a return of contamination, shown below. This contamination is visible over the entire wafer, but is easiest…
We have seen before that in petri dishes, flipped samples (well side up) discolor faster as compared to the ‘membrane side up’ samples. This could be due to local environment trapped below the chip. Hence, I used Sepcon format so that the sample is raised above the floor to avoid any trapped solution below it….
I’ve taken fluorescence measurements with the fluorescence microscope on PEGylated and unPEGylated glass coverslips and SiN chips. Six coverslips and six chips were prepared. Samples were treated exactly the same, save for the fact that half the samples had PEG Silane in their treatment and half did not (though they were still bathed in toluene…
Given the results of my previous post, I am reworking my design to make it more manufacturable. BBB Device V2-6 Compressed The major change compared to my last design is the inclusion of a full length microscope slide and coverslip. Instead of cleaving the electrodes from the glass, this step eliminates the need to…
In order to test the sealing of the capillary tubing the PDMS I made a batch of PDMS with a recess in it (from a dime). Once this cured I used the UV Ozone process (@25C) to bond the PDMS to a glass microscope slide. When I arrived this morning the system was fully bound….