The following is a public service announcement:
I’ve just aliquoted about 40mL of fluorescent BSA and placed it in the freezer. Each aliquot contains roughly 1mL of 6mg/mL TRITC-conjugate BSA, so there’s plenty of them. If anyone needs fluorescent BSA for anything, feel free to take as much as you need from the box labeled “TRITC-conjugate BSA” in the freezer.
This has been a public service announcement.
Quick review of “Achieving more frequent and longer dialysis for the majority: wearable dialysis and implantable artificial kidney devices” by Fissell, Roy, and Davenport see Fissell(Roy)_2013_International_Kidney.pdf in the hemodialysis section of the library. First a little background: Two type of wearable devices: Peritoneal Dialysis (PD) and Hemodialysis (HD) In PD, dialysate is pumped into and…
Samples are from wafers #316 and 318. This is the first time for wafer scale deposition. Processing conditions:1) chamber base pressure @ 6×10-7 Torr (previously @ 5×10-6 Torr)2) 15nm Ti + 15nm Au, no vacuum break Estimated “cell resistance”: about 20-25 ohm, much lower than previous measurement. Possible reasons why lower resistance is observed:1) “Au…
Today while I was imaging a Al2O3 coated pnc-Si membrane on the high-res TEM, I noticed something curious as I placed the beam on a single pore for a few minutes. I was initially interested in the structure of the aluminum oxide coating, but found that something started to deposit on the pore walls as…
To follow up on some of Dave’s work – I was curious if the ALD alumina affects the strength of pnc-Si membranes. Punchline: 2.5 nm of Alumina seems to increase the burst pressure, while 5.0 nm reduces the burst pressure. Methods: As part of routine QC, we had already measured robustness on 6 SepCons to…
The basic principle of inducing the osmotic pressure to suppress back pressure is based on the counterbalance of the opposing flows of solvent. Consider an electrolytic cell composed of a pair of Ag/AgCl electrodes and a Nafion-coated pnc-Si membrane separating NaCl solution into two halves. Initially, the electrolyte in either half has the same concentration…
With the new heater installed in the AJA sputter tool, the production team decided to run a set of wafers at six different chamber temperatures to re-characterize membrane morphology, mechanical strength and overall quality of material. These films were all deposited with 25 W substrate bias and annealed at 1000 C in the RTP with…
Comments are closed.
Please don’t post local messages under the ‘data’ category. Those get broadcasted out to all subscribers including those at RIT or in the UK who could care less where we put the fluorescent BSA.
The correct category for this type of helpful information is ‘URNews.’
Oh no, I’m sorry! I forgot that we had multiple categories. I’ll be more careful in the future.
Sorry to anyone who was sent this message due to my mistake!