Spectrophotometer raw data
Upload just for future reference. This includes the data of KMnO4 serial dilutions absorbance and the stir cell diffusion experiment.
Similar Posts
Separations with NPN at varied concentrations
We are carrying out filtrations using wafer 1085. We are testing the total volume of filtrate that passes in a given time. We expect the total filtrate volume to decrease as concentration increases due to more immediate clogging. Ultimately, we want to show that we can get higher total volumes of filtrate in the reverse…
SiO2 coated membranes
The SiO2 coated samples (from W335 & W341) were found completely discolored after 5 days in DMEM (benchtop). Thus, silicon dioxide coating didn’t prevent discoloration as much as the RTP treatment. There’s a need to check the discoloration profile of the SiO2 coated samples within 5 days. Till 24 hrs. there was no discoloration observed….
Effect of NHS- PEG8 modified surfaces on the adsorption of proteins (BSA)
The AIM of this experiment was to see the effect of surfaces modified with PEGs (Polyethylene glycol) to protein adsorption. The PEG that I used for the current study is MS-PEG8 (Methyl-PEG8-NHS) which is Amine reactive. Method: For the current experiment I used planar silicon chips which have ~ 142 nm of thermally grown oxide….
ASDC Characterization on PDMS Substrates
Conventional tissue culture substrates do not accurately emulate in vivo surface conditions. This project involves the development and characterization of a polydimethylsiloxane (PDMS) substrate for cell culture. PDMS is an important biomaterial due to its optical transparency, biocompatibility, and variable elastic modulus. ADSCs and HUVECs were used to analyze spreading and proliferation on PDMS-based substrates of…
W612 Characterization
I tested W612 for air permeability and burst pressure, shown below. It should be noted that the air permeability and burst pressure values are comparable to W504; looks like a good reproduction! I also tested a sample with the hexane residue and debris, no difference in permeability or burst pressure was seen. Background pores included…
Running SolidWorks 2025 on an Apple Silicon Mac with VMware Fusion: A Complete Setup Guide
If you’re a researcher or student using SolidWorks on an Apple Silicon Mac, you’ve probably run into the same wall: SolidWorks doesn’t officially support virtualized environments, and getting it to run stably in VMware Fusion takes some work. After extensive troubleshooting, here is the complete step-by-step protocol that got SolidWorks 2025 running on an M5…
One Comment
Comments are closed.
This belongs in a notebook. Data on the blog does not need to be polished, but it should in a form that communicates a result to others. If everyone uploaded their rawest data, the blog would be unbearable to read.