I tested four samples (-1,1); (-1,2); (-1,3); and (-2,4) for air permeability and burst pressure. The first three samples showed no measurable air permeability for three attempts each. The sample from position (-2,4) did have a very small air permeability of 11.2 cc/(cm2*atm). Based on the results of rhodamine diffusion it seems odd that I…
One area of use to explore for the membranes is desalting, the removal of salts from solutions (such as those containing proteins). Two dialysis products made my Thermo/Pierce were tested to develop a protocol and test manufacturer’s claims. These products are the mini-dialysis unit on the left and the dialysis cassette on the right; both…
HUVEC adhesion was measured on glass, tissue culture plastic, and pnc-Si, with poly-lysine coated plastic and teflon coverslips as positive and negative controls. Adhesion on pnc-Si was low, this could be due to cells being lost through broken slits or possibly some other unknown factor. Adhesion tests are continuing, with the use of solid Si…
Two more adhesion tests were run recently, one on Tuesday and one on Wednesday. For both tests cells were imaged after five hours. Fibroblast trial 3 was the first test where the optimal cell density (assuming 100% of cells are detached by trypsin and 100% attach to the substrate) was measured using a hemacytometer. Of…
Thus far three HUVEC and two L13T3 growth tests have been conducted on substrates including glass,pnc-Si, tissue culture plastic, and untreated plastic. Only one test with untreated plastic has been run for each cell type. Cells on Si samples are not on the slits but rather on substrate surrounding. It seems that HUVEC proliferate more…
Mike and I tested the movement of Rhodamine between the two cell channels to prove that the Rhodamine particles do diffuse through the membrane. After inspection in the microscope we saw that the fluorescence from the Rhodamine does transfer from one channel to the other across the membrane. However, we also noticed that the Rhodamine…
Adhesions tests are being performed to see if cellular attachment varies between our material, glass, and plastic. These experiments are motivated by lower initial cell densities observed on pnc-Si in growth tests; we are investigating if the lower initial densities are due to the cells rolling of the edge of the raised pnc-Si substrate or…
A third fibroblast (L1 3T3, P22) growth test was conducted using glass, untreated and tissue culture treated plastic, and RTPed pnc-Si (W509) as substrates. Cells were grown in DMEM +10% FBS changed every 48 hours. R values are for the fit N=No*exp^(r*t), where r has units of divisions/hour. For this trial fibroblasts grown on glass,…
W502 and 504 were tested for burst pressure and air permeability. Only one sample from W502 was tested for burst pressure (the other broke while setting up and I wanted to conserve samples) with a burst pressure of 4.46 psi. The burst pressures for W504 ranged from 2.06 to 6.57 (n=3). Air permeability is shown…
A second fibroblast (L1 3T3, P21) growth test was conducted on RTP treated samples from W510, tissue culture plastic (polystyrene), and glass cover slips. Fibroblasts were cultured in DMEM with media changed every 48 hours. Cells were imaged using the live/dead assay. Fibroblasts divided every 29.9, 35, and 37.7 hours when grown on pnc-Si, glass,…