Latest Water Permeability Figure for PES Membranes

In my last diffusion experiment, I used wafer SC 442. The results seemed to show that IgG was indeed diffusing through the membrane. As a follow up experiment, I am trying to show that I can pass IgG through more than just the one membrane. Furthermore, SC 505 has a much larger average pore size…

I tried to measure the thickness of the non-carbonized and carbonized membranes for the paper using SEM. To have a clear cut of the membrane I place the membrane chip upside down on a silicon wafer piece, then bend the membrane chip with tweezers so the membrane sticks to the wafer while breaking of the…

Last week I etched three wafers of different silicon thicknesses (10 nm, 15 nm, 20 nm). All the wafers had a TEOS mask with the standard three layer sputtered film on the front. Not that surprising is the fact that the thinnest membrane showed pores while the 15 and 20 nm membranes did not at…

Tom prepared two PVP coated TEM samples for me to image today. One of the samples was washed with dH20 and the other left untouched. Below is a series of three images, from left to right: no PVP, PVP no wash, PVP & wash. I wasn’t able to tell any differences under the River Campus…

Hi all, We have already showed in our earlier [ post ] that our shear-free chemotaxis system can indeed elicit chemotaxis, suggesting that we have successfully translated a gradient through the membrane to the shear-free side of the system where the cells reside.  However, it is still nice to show via fluorescence how the translated gradient looks…

I mixed made solutions of PBS and Rhodamine with varying Rhodamine concentrations and ran them through the spectrometer. Below is the concentration vs absorption curve I made from it. I blanked the spec with PBS instead of ddH2O since the solution is in PBS. The slope is almost double for Rhodamine in ddH2O compared to…