Multi channel, dual chip dialysis device

I measured the I-V characteristics of our coated membranes on Wed. at RIT. JP observed the measurement. The semicon parameter analyzer in the test lab is “old” but isexactly what we need! Roughly speaking, our coated membraneshave resistance about 2k Ohm, depending on the thicknesses ofmetal films (this is based on pure Ti coated samples,…

The last time I did live imaging on the confocal microscope was in December of 2019. Then I was imaging the capture of 1.24 µm diameter beads in 1 µm slit pore membranes to visualize the difference between steric and affinity based capture. This time around, all of the materials are different, but the process…

The goal of this rotation was to create a device to test the electro-osmotic properties of the membrane bound silicon chips. To perform this task, it was necessary to attach two glass pipettes onto both sides of a chip. The method required that the protocol be repeatable and easy to perform. Although it appears to…

In our last post we showed that this latest wafer with 36 nm pores did a better job of blocking 20 nm NPs in the forward and reverse orientations, whereas an older wafer (1070- 45 nm, 15%) showed better separations in reverse orientation.  Here is a couple plots summarizing the difference: So 20 nm NPs…

On Friday, Henry was kind enough to ship 15 tested Sepcons to the Barcikowski group in Essen, Germany. With luck they will arrive in time for Christmas. I wrote up some documentation and an illustration for wetting and using the Sepcons and figured I would share it with the group. Unfortunately, wordpress won’t let me…